Ntibisanzwe isi oxyde yttrium ifu ya 1314-36-9
Yttrium Oxide Intangiriro ngufi
Inzira (Y2O3)
CAS No.: 1314-36-9
Isuku: 99,999%
SSA: 25-45 m2 / g
Ibara: cyera
Morphologiya: serefegitura
Ubucucike bwinshi: 0.31 g / cm3
Ubucucike nyabwo: 5.01 g / cm3
Uburemere bwa molekuline: 225.81
Ingingo yo gushonga: dogere selisiyumu 2425
Kugaragara: Ifu yera
Gukemuka: Kudashonga mumazi, gushonga muburyo bugaragara muri acide minerval ikomeye
Igihagararo: Hygroscopique gahoro
Porogaramu Yttrium
1: Yttrium Oxide, nanone yitwa Yttria, isuku ryinshi Yttrium Oxide nibikoresho byingenzi kuri tri-band Rare Earth fosifori itanga ibara ritukura muri tereviziyo yamabara & tebes ya mudasobwa.
2: Mu nganda za optique, Oxide ya Yttrium ikoreshwa mu gukora Yttrium-Iron-Garnets, ikora neza cyane ya microwave.
3: Ubuziranenge buke bwa Yttrium Oxide bukoreshwa cyane mububiko bwa elegitoroniki.Irakoreshwa cyane mugukora Eu: YVO4 na Eu: Y2O3 fosifori itanga ibara ritukura mumabara ya TV yamashusho.
4: Oxide Yttrium nayo ikoreshwa mugukora Yttrium-Iron-Garnets, ikora neza cyane ya microwave.
INGINGO | UMWIHARIKO | IBISUBIZO BY'IKIZAMINI | ||||||
Y2O3 / TREO (%, min) | 99.995 | 99.999 | ||||||
TREO (%, min) | 98 | 98.38 | ||||||
Ingano ya Particle | 30-60nm, 1.0-2.0um, 0.3-0.6um, 0.6-1.0um | Hindura | ||||||
RE Impanuka (/ REO,%) | ||||||||
La2O3 | ≤0.0005 | ≤0.0001 | ||||||
CeO2 | ≤0.0005 | ≤0.0001 | ||||||
Pr6O11 | ≤0.0002 | ≤0.0001 | ||||||
Nd2O3 | ≤0.0002 | ≤0.0001 | ||||||
Sm2O3 | ≤0.0002 | ≤0.0001 | ||||||
Eu2O3 | ≤0.0002 | ≤0.0001 | ||||||
Gd2O3 | ≤0.0002 | ≤0.0001 | ||||||
Tb4O7 | ≤0.0002 | ≤0.0001 | ||||||
Dy2O3 | ≤0.0002 | ≤0.0001 | ||||||
Ho2O3 | ≤0.001 | ≤0.0001 | ||||||
Er2O3 | ≤0.001 | ≤0.0001 | ||||||
Tm2O3 | ≤0.0001 | ≤0.00002 | ||||||
Yb2O3 | ≤0.0001 | ≤0.00002 | ||||||
Lu2O3 | ≤0.0001 | ≤0.00002 | ||||||
LOI | ≤2% |